产品标准
|
钢种
|
σ 0.2 (Mpa)
|
σ b (Mpa)
|
δ 5 (%)
|
硬度
|
备注
|
ASTM A312 ASTM A213 | 304 304H | ≧205 | ≧515 | ≧ 35 | ≦ 90HRB | a |
310S 316 | ||||||
317L 321 | ||||||
321H 347 | ||||||
347H | ||||||
304L 316L | ≧ 170 | ≧ 485 | ||||
ASTM A511 | 304L 316L | ≧ 205 | ≧ 515 | |||
ASTM A790 | S318003(2205) | ≧ 450 | ≧ 620 | ≧ 25 | ≦ 30.5HRC | a |
DIN 17456 DIN17458 | 1.4301 | ≧ 195 | 500~700 | ≧ 40 | / | σ 1.0 ≧230(Mpa) |
1.4401 | ≧ 205 | 510~710 | σ 1.0 ≧240(Mpa) | |||
1.4404 | ≧ 190 | 490~690 | σ 1.0 ≧225(Mpa) | |||
1.4541 | ≧ 180 | 460~680 | ≧ 35 | σ 1.0 ≧215(Mpa) | ||
JIS G3459 JIS G3463 | 304 304H | ≧205 | ≧ 520 | ≧ 35 | ≦ 90HRB | a |
310S 316 | ||||||
316H 317 | ||||||
321 321H | ||||||
347 347H | ||||||
304L 316L 317L | ≧175 | ≧ 480 | ≧ 35 | |||
GB/T14975 GB/T14976 GB13296 GB5310 | 0Cr18Ni9 | ≧ 205 | ≧ 520 | ≧ 35 | ≦ 90HRB | a |